前言：PC LNP LUBRICOMP DFL36P
LNP? LUBRICOMP? DFL36PPC(聚碳酸酯)沙特基础 (SABIC)产品描述LNP* LUBRICOMP* DFL36P is a compound based on Polycarbonate containing 30% Glass Fiber 15% PTFE. Added features of this material include:Exceptional Processing. Wear Resistant产品特性耐磨易成型填充增强增强填充30% 玻纤15% PTFE45% 玻纤+PTFE技术参数物理性能值/单位测试标准测试条件密度1.56 g/cm?ISO 1183密度1.56 g/cm?ASTM D792收缩率纵向(Flow)0.2~0.4 %ASTM D 955flow, 24 hrs横向(Across Flow)0.3~0.5 %ASTM D 955xflow, 24 hrs吸湿率0.11 %ISO 6223°C / 50% RH吸湿率0.07 %ASTM D 57050% RH, 24 hrs机械性能值/单位测试标准测试条件拉伸强度断裂(brk)112 MpaISO 5275 mm/min断裂(brk)113 MpaASTM D638Type I, 5 mm/min拉伸延伸率屈服(yld)2.2 %ASTM D638Type I, 5 mm/min断裂(brk)2.8 %ASTM D638Type I, 5 mm/min断裂(brk)2.1 %ISO 5275 mm/min弯曲强度断裂(brk)176 MpaASTM D7901.3 mm/min, 50 mm span-172 MpaISO 178弯曲模量8920 MpaASTM D7901.3 mm/min, 50 mm span弯曲模量8830 MpaISO 1782 mm/min拉伸模量9770 MpaASTM D63850 mm/min拉伸模量9520 MpaISO 5271 mm/min摩擦系数0.47 -ASTM D 3702Dynamic COF摩擦系数0.52 -ASTM D 3702Static COF磨损因数14 E-10 in5·min/ft·lb·hrASTM D 3702Wear Factor Ring磨损因数96 E-10 in5·min/ft·lb·hrASTM D 3702Wear Factor Washer冲击性能值/单位测试标准测试条件悬臂梁缺口(Izod Notched)23℃ (73℉)132 J/mASTM D25623℃ (73℉)13 kJ/m?ISO 180/1A80*10*4悬臂梁无缺口(Izod Unnotched)23℃ (73℉)689 J/mASTM D481223℃ (73℉)42 kJ/m?ISO 180/1U80*10*4仪器化落镖冲击能量23℃ (73℉)总能量17 JASTM D3763多轴冲击5 JISO 6603热学性能值/单位测试标准测试条件热变形温度(HDT)0.45 Mpa (66 psi)（4.6kg/cm?）137 °CASTM D6483.2 mm, unannealed0.45 Mpa (66 psi)（4.6kg/cm?）138 °CISO 75/BfFlatw 80*10*4 sp=64mm1.8 Mpa (264 psi)（18.6kg/cm?）133 °CASTM D6483.2 mm, unannealed1.8 Mpa (264 psi)（18.6kg/cm?）133 °CISO 75/AfFlatw 80*10*4 sp=64mm线性膨胀系数(CLTE)纵向(Flow)3.0E+7 E-6/°CASTM D 696-30°C to 30°C, flow横向(Across Flow)6.5E+7 E-6/°CASTM D 696-30°C to 30°C, xflow